硅酮結構膠施工過(guò)程中有四個(gè)常見(jiàn)問(wèn)題：粘接不良，固化慢，結構膠粘接寬度不夠，結構膠體里面有氣泡。如何避免雙組分硅酮結構膠混合不均勻?
There are four common problems in the construction of silicone structural adhesive: poor bonding, slow curing, insufficient bonding width of structural adhesive, and bubbles in the structure colloid. How to avoid the inhomogeneous mixture of two component silicone structural adhesives?
雙組分硅酮結構膠是由主劑A組分(白膠)和固化劑B組分(黑膠)組成，通過(guò)雙組分打膠機，按廠(chǎng)家的比例混合均勻后使用?；旌虾蟮慕Y構膠經(jīng)過(guò)一段時(shí)間固化，終獲得好的粘接性能和物理性能。但是，如果結構膠混合不均勻后使用，結構膠固化就會(huì )出現質(zhì)量問(wèn)題。
The two-component silicone rubber structure is composed of main agent A component (glue) and curing agent B component (black glue), glue machine by two components, according to the manufacturer's recommended mixing ratio after use. After a period of time curing, the mixed structural adhesive has good bonding and physical properties. However, the quality problem will occur when the structural adhesive is used after the mixing is not uniform.
結構膠混合不均勻，局部會(huì )出現白色條紋。在光線(xiàn)比較亮的情況下，更加容易觀(guān)察。結構膠固化后的強度下降，固化交聯(lián)不完全、嚴重時(shí)候會(huì )發(fā)粘，無(wú)法固化等。
The mixing of the structural adhesive is not uniform, and the white stripes appear in the part. It is easier to observe when the light is brighter. After curing, the strength of the adhesive is decreased, the curing crosslinking is not complete, when it is serious, it will be sticky and can not be cured.
我們會(huì )用優(yōu)良的、貼切的服務(wù)，讓顧客感受到親情般的溫暖，始終視顧客的如己如親。我們會(huì )用自然優(yōu)勢打造產(chǎn)品的獨特之處，從而給消費者帶來(lái)享用產(chǎn)品時(shí)獨特的心境。
We will use a good, appropriate service, let customers feel the warmth of family like, always look at the safety of customers as if they are friendly. We will use the natural advantage to create the unique features of the product, so as to give consumers the unique mood to enjoy the product.
上一篇：點(diǎn)膠量的膠量不均勻出現的原因？
下一篇：選擇中空玻璃生產(chǎn)線(xiàn)的注意事項